Steel Fibre
|
|
STEEL FIBRE
MATERIALS
Steel Fibre dalam
berbagai bentuk antara lain
1.
Melt Extract Fibre
2.
Cold Drawn
Fibre
3.
Stainless
Steel Wool
Material ME Fibre, Cold
Drawn Fibre dan Stainless Steel Wool bisa dibuat dengan menggunakan material
SUS 430, SUS 446, SUS 304, SUS 310, SUS 316 maupun SUS 330.
Specifications:
|
Grades
|
330
|
310
|
304
|
446
|
430
|
430A*
|
|
Chemical
Composition
|
C
|
0.5
|
0.50
|
0.50
|
0.40
|
0.40
|
0.40
|
|
P
|
0.05
|
0.05
|
0.05
|
0.05
|
0.05
|
0.05
|
|
Mn
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
2.0
|
|
Si
|
3.5
|
3.5
|
3.5
|
3.5
|
3.5
|
3.5
|
|
Cr
|
17.0 – 20.0
|
24.0 – 26.0
|
18.0 – 20.0
|
23.0 – 27.0
|
14.0 – 18.0
|
14.0 – 18.0
|
|
Ni
|
34.0 – 37.0
|
19.0 -
22.0
|
8.0 – 10.5
|
0.5
|
0.5
|
0.5
|
|
Al
|
-
|
-
|
-
|
-
|
-
|
2-4
|
|
Melt temperature oC
|
1343 - 1425
|
1400 – 1455
|
1400 – 1455
|
1425 – 1510
|
1480 – 1530
|
1520 – 1560
|
|
Thermal conductivity (540°C) W/m2K
|
28.50
|
20.1
|
21.5
|
24.8
|
26.5
|
|
|
Coefficient of thermal expansion (870°C) @10-6/oC
|
17.6
|
18.50
|
20.2
|
13.1
|
13.7
|
|
|
Critical Oxidation Temperature
|
Cyclic heating
|
1050oC
|
1040oC
|
870°C
|
1100oC
|
850oC
|
|
|
Continuous Service
|
1165oC
|
1200oC
|
1100°C
|
1200oC
|
1000oC
|
|
|
Tensile Strength
|
20°C
|
480 MPa
|
540 MPa
|
515 MPa
|
900 Mpa
|
850 Mpa
|
|
|
870°C
|
31 Mpa
|
152 MPa
|
124 Mpa
|
53 Mpa
|
47 Mpa
|
|
|
Modulus of Elasticity (24oC)
|
196 Gpa
|
125 GPa
|
124 GPa
|
97 Gpa
|
83 Gpa
|
|
|
|
|
|
|
|
|
|
|
Grade 430A merupakan
jenis ME Stainless Steel Fibres yang banyak digunakan di Jepang. Mengandung
alumunium dan mempunyai melting point yang lebih tinggi dari yang lainnya.
Keuntungan grade 430 A
adalah mempunyai tingkat kondensasi yang lebih rendah, kekerasan yang lebih
tinggi, kemampuan gesek yang lebih tinggi dan mempunyai kemampuan tahan
terhadap oksidasi dari grade lainnya (sekitar 3-6 kali).
|
Untuk informasi lebih lanjut bisa
menghubungi Sales Engineer kami, atau bisa menghubungi kami secara langsung
atau disini.